[1]马立云,单传丽,赵凤阳,等.澄清剂对高铝硅酸盐玻璃的澄清效果研究[J].燕山大学学报,2018,42(1):053-58.[doi:10.3969/j.issn.1007-791X.2018.01.009]
 Research on clarification of refining agent on high alumina silicate glass.Research on Clarification of refining agent on high alumina silicate glass[J].Journal of YanShan University,2018,42(1):053-58.[doi:10.3969/j.issn.1007-791X.2018.01.009]
点击复制

澄清剂对高铝硅酸盐玻璃的澄清效果研究
分享到:

《燕山大学学报》[ISSN:1007-791X/CN:13-1219/N]

卷:
42
期数:
2018年第1期
页码:
053-58
栏目:
材料科学与工程
出版日期:
2018-03-31

文章信息/Info

Title:
Research on Clarification of refining agent on high alumina silicate glass
文章编号:
1007-791X(2018)01-0053-06
作者:
马立云12单传丽12*赵凤阳12曹  欣12石丽芬12
1.浮法玻璃新技术国家重点实验室,安徽 蚌埠 233000;2.蚌埠玻璃工业设计研究院,安徽 蚌埠 233018
Author(s):
Research on clarification of refining agent on high alumina silicate glass
1.State Key Laboratory of Advanced Technology for Float Glass,Bengbu,Anhui 233000,China;2.Bengbu Design & Research Institute for Glass Industry,Bengbu,Anhui 233018,China
关键词:
高铝硅酸盐玻璃澄清剂气泡
Keywords:
high alumina silicate glassclarifying agentbubble
分类号:
TQ171
DOI:
10.3969/j.issn.1007-791X.2018.01.009
文献标志码:
A
摘要:
高铝硅酸盐玻璃组成中Al2O3的含量一般大于10%以上,是近年来发展的一种新型玻璃,有着优良的热力学性能,尤其在硬度、韧性和抗划伤等方面表现突出,是电子信息产品的触摸屏幕和手写屏的优选保护材料。本文研究了澄清剂的种类和含量对高铝硅酸盐玻璃澄清效果的影响,定量地研究了在澄清过程中气泡熔占比、气泡直径平均尺寸、气泡个数的变化,研究分析了适合高铝硅酸盐玻璃的澄清方案。结果表明:在1 600 ℃熔化温度下,Na2SO4的澄清效果要明显优于SnO2,当Na2SO4含率为2.0%时高铝硅酸盐玻璃的澄清效果最佳。
Abstract:
The high alumina silicate glasses with Al2O3 content more than 10% has been developed as a new type of glass in recent years with excellent properties such as outstanding hardness,toughness and scratch resistance,etc.Meanwhile,it serves as a promising protection material for touching screen and handwriting screen of electronic information products.The influence of the type and content of the refining agents on the properties of the high alumina silicate glass were investigated.The bubble fusion ratio in the process of clarification,the average size of bubble diameter,and the variation of bubble number are discussed.A reliable scheme for clarification was designed for the high aluminum silicate glasses,indicating that the melt treatment of 1 600 ℃ and the content of 2% Na2SO4,are critical.

相似文献/References:

[1]谢君樑,和阿雷,赵高凌,等. 高铝硅酸盐玻璃的化学强化及其结果拟合[J].燕山大学学报,2018,42(1):034.[doi:10.3969/j.issn.1007-791X.2018.01.005]
 XIE Junliang,HE Alei,ZHAO Gaoling,et al.Chemical strengthening of high aluminosilicate glasses and experimental fitting[J].Journal of YanShan University,2018,42(1):034.[doi:10.3969/j.issn.1007-791X.2018.01.005]

备注/Memo

备注/Memo:
收稿日期:2017-05-20      责任编辑:王建青
基金项目:安徽省科技重大专项计划项目(15czz02004);国家重点研发计划资助项目(2016YFB0303700); 硅酸盐建筑材料国家重点实验室开放基金项目( SYSJJ2017-14)
作者简介:马立云(1964-),男,山东烟台人,教授级高级工程师,主要研究方向为新型玻璃、功能薄膜等;*通信作者:单传丽(1983-),女,安徽滁州人,高级工程师,主要研究方向为特种玻璃的澄清脱泡,Email:shanchuanli930@163.com
更新日期/Last Update: 2018-04-23